Product Parameters
(1Polyeater Needle Felt
Polyester needle-punched filter cloth is a fine fiber filter material produced by non-woven needle-punching technology, with fibers arranged in an interlaced manner and uniform pore distribution. This filter cloth is made from polyester short fibers and twisted yarns. After undergoing post-treatment such as hot rolling, scouring, or coating, its surface becomes smooth and flat, making it less prone to being clogged by dust. This filter material has a large porosity, good air permeability, and is widely used in various fields. It has strong chemical stability and is an ideal filtering material for normal temperature working conditions and gas-solid separation applications.
| Name |
Polyester Needle Felt |
| Material |
Polyester fiber/polyester staple fiber base fabric or polyester filament base fabric |
| Weight |
500~600±5%g/m² |
| Air permeability |
8-20m³/m².min |
| Radial tensile force |
>800N/5×20cm |
| Weft tensile force |
>1000N/5×20cm |
| Extend in the radial direction |
<35% |
| Extension in the weft direction |
<50% |
| Working Temperature |
Long time 80ºC~130ºC, Short time 150ºC |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
Singeing, calendering, shaping, flame retardancy, water resistance or film coating treatment |
During the operation of bag-type dust collectors, for dust in the air that contains a large amount of moisture and oil, as well as hygroscopic and easily deliqueshable dust, a water film may form on the surface of the dust, thereby increasing adhesion. Although this is helpful for dust capture, it will make dust cleaning difficult, especially when in a high-humidity state, condensation may occur due to the cooling effect of the external gas. This not only causes the collected dust to form scale on the surface of the filter material and thus clog it, but also increases the operating resistance of the dust removal equipment, directly affecting the normal operation of the dust removal equipment. Water-repellent and oil-proof needled felt can effectively prevent water and various oil contaminants from adhering and penetrating. Compared with ordinary filter materials, it not only has oil-proof and oil-proof properties, but also has anti-caking and easy-to-peel properties for dust.
| Name |
Water and Oil Proof Polyester Needle Felt
|
| Material |
Polyester fiber/polyester staple fiber base fabric or polyester filament base fabric |
| Weight |
500~600±5%g/m² |
| Air permeability |
8-20m³/m².min |
| Radial tensile force |
>800N/5×20cm |
| Weft tensile force |
>1000N/5×20cm |
| Extend in the radial direction |
<35% |
| Extension in the weft direction |
<50% |
| Working Temperature |
Long time 80ºC~130ºC, Short time 150ºC |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
Singeing, calendering, shaping, flame retardancy, water resistance or film coating treatment |
,,Product Description:
When the concentration of industrial dust reaches a certain level (i.e., the explosion limit), if it encounters factors such as static discharge sparks or boundary ignition, it is very likely to cause explosions and fires. For example, coal dust, chemical dust, explosive dust, etc. There is a possibility of explosion in case of static discharge. In the field of bag-type dust removal, if these dusts need to be collected by bags, the bags themselves are required to have anti-static functions. In addition to the production process of ordinary needled felt, the production of anti-static filter materials also requires the incorporation of conductive fiber yarns into the base fabric warp yarns for the production of needled felt.
| Name |
Water and Oil Proof, Anti-Static Polyester Needle Felt
|
| Material |
Polyester fiber/polyester conductive base fabric |
| Weight |
500~600±5%g/m² |
| Air permeability |
8-20m³/m².min |
| Radial tensile force |
>800N/5×20cm |
| Weft tensile force |
>1000N/5×20cm |
| Extend in the radial direction |
<35% |
| Extension in the weft direction |
<50% |
| Electrical resistance surface |
4.8×109 |
| Volumetric resistance |
8.7×109 |
| Frictional potential (maximum value) |
250 |
| Frictional potential (average value) |
183 |
| Surface electric nuclear density mc/ |
3.4 |
| Working Temperature |
Long time 80ºC~130ºC, Short time 150ºC |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
Singeing, calendering, shaping, flame retardancy, water resistance or film coating treatment |
,,.,,When the concentration of industrial dust reaches a certain level (i.e., the explosion limit), if it encounters factors such as static discharge sparks or boundary ignition, it is very likely to cause explosions and fires. Such as: coal dust, chemical dust, explosive dust, etc. There is a possibility of explosion in case of static discharge. In the field of bag-type dust removal, if these dusts need to be collected by bags, the bags themselves are required to have anti-static functions. In addition to the production process of ordinary needled felt, the production of anti-static filter materials also requires the addition of conductive fibers and other materials during the production of needled felt.
,,.,
| Name |
Blended Anti-Static Polyester Needle Felt
|
| Material |
Polyester fiber, conductive fiber/polyester conductive base fabric |
| Weight |
500~600±5%g/m² |
| Air permeability |
8-20m³/m².min |
| Radial tensile force |
>800N/5×20cm |
| Weft tensile force |
>1000N/5×20cm |
| Extend in the radial direction |
<35% |
| Extension in the weft direction |
<50% |
| Electrical resistance surface |
5.0×109 |
| Volumetric resistance |
9.9×109 |
| Frictional potential (maximum value) |
250 |
| Frictional potential (average value) |
183 |
| Surface electric nuclear density mc/ |
3.4 |
| Working Temperature |
Long time 80ºC~130ºC, Short time 150ºC |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
Singeing, calendering, shaping, flame retardancy, water resistance or film coating treatment |
,..Product Description:
Acrylic needle-punched felt is made by non-woven needle-punching technology, which utilizes the interlaced arrangement of strong acrylic fibers with uniform pore distribution. The surface of the fine fiber filter material is treated with hot rolling, singeing, etc., making it smooth and flat, and not easily clogged by dust. This filter material has large pores. It has good air permeability and strong chemical stability. It can not only filter gases at normal temperature but also has good hydrolysis resistance. This product is applicable to the field of flue gas filtration with high water content such as cement slag particles.
,,
| Name |
Acrylic Needled Felt
|
|
| Material |
Acrylic fiber/acrylic base fabric |
|
| Weight |
500~600±5%g/m² |
|
| Air permeability |
8-20m³/m².min |
|
| Radial tensile force |
>800N/5×20cm |
|
| Weft tensile force |
>1000N/5×20cm |
|
| Extend in the radial direction |
<25% |
|
| Extension in the weft direction |
<50% |
|
| Working Temperature |
Long time 80ºC~130ºC, Short time 150ºC |
| Treatment |
Singeing, calendering, shaping, flame retardancy, water resistance or film coating treatment |
,.PPS needled felt is made by needling 100% PPS fibers. PPS fibers, with their excellent acid and alkali resistance, oxidation resistance, wear resistance and folding resistance, enable the composite felt to withstand a normal temperature of up to 160ºC and a short-term temperature of up to 190ºC. It is suitable for fields with high sulfur content such as flue gas filtration in thermal power and coal-fired boilers
| Name |
PPS Needle Felt |
|
| Material |
PPS Fiber /PPS Base Fabric |
|
| Weight |
500~600±5%g/m² |
|
| Air permeability |
8-20m³/m².min |
|
| Radial tensile force |
>800N/5×20cm |
|
| Weft tensile force |
>1000N/5×20cm |
|
| Extend in the radial direction |
<30% |
|
| Extension in the weft direction |
<30% |
|
| Working Temperature |
Long Time 180ºC, Short Time 200ºC |
| Acid resistance |
Perfect |
| Alkali resistance |
Perfect |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
Singeing, calendering, shaping, flame retardancy, water resistance or film coating treatment |
In the field of bag filter, for industries with relatively high flue gas temperatures, chemical fibers capable of withstanding high temperatures are needed to manufacture filter materials, which can fully meet the high-temperature working conditions of 150-220ºC. Inmetas fibers belong to aromatic polyamide fibers, which have excellent heat resistance, wear resistance and folding resistance. Their folding resistance is irreplaceable by glass fibers. It is applicable to industries such as asphalt mixing, steel, cement, and non-ferrous metal smelting.
Product Description:
FMS needled felt is a new type of high-temperature and high-efficiency composite fiber material with a reasonable structure and excellent performance. It not only has the advantages of glass fiber woven filter material such as high temperature resistance, corrosion resistance, dimensional stability and high strength, but also is made from 100% alkali-free glass fiber as raw material, using high-count glass fiber filaments and needling them into fibers. It has good heat resistance, flame retardancy and anti-corrosion effects. It has low gas resistance, a dust removal efficiency higher than that of woven filter materials, and a filtration speed about twice as high as that of woven filter materials. It is currently the preferred product for purifying blast furnace gas and flue gas filtration in the steel, smelting and other industries.
| Nane |
FMS Needle Felt
|
|
| Material |
P84, PTFE, Aramid Or PPS Fibers, Glass Fiber/Glass Fiber Base Fabric |
|
| Weight |
950±105g/m² |
|
| Air permeability |
15-25m³/m².min |
|
| Radial tensile force |
>1150N/5×20cm |
|
| Weft tensile force |
>1150N/5×20cm |
|
| Extend in the radial direction |
<10% |
|
| Extension in the weft direction |
<10% |
|
| Working Temperature |
Long Time 260ºC, Short Time 280ºC |
| Acid resistance |
Perfect |
| Alkali resistance |
Perfect |
| Filteration Air Speed |
≤1.0m/min |
| Filteration Efficiency |
99.99% |
| Treatment |
PTFE Impregnation, Film Coating Or Coating Treatment |
Product Description:
P84 needled felt is made from P84 fibers (i.e. polyimide fibers) produced by LENZING Company of Austria through three-dimensional treatment
It is needle-punched and has excellent high-temperature resistance, with a temperature resistance of up to 260ºC. Moreover, the cross-section of P84 fibers is irregular leaf-shaped, which can significantly enhance the filtration effect. The fibers themselves also have certain resistance to hydrolysis and oxidation. This product has good temperature resistance and filtration effect, and is widely used in complex working conditions such as the kiln head and kiln tail of cement plants, waste incineration, and coal-fired boilers.
| Nane |
P84 Needle Felt |
|
| Material |
P84 fiber /P84 base fabric or PTFE base fabric |
|
| Weight |
500~600±5%g/m² |
|
| Air permeability |
15-25m³/m².min |
|
| Radial tensile force |
>800N/5×20cm |
|
| Weft tensile force |
>1000N/5×20cm |
|
| Extend in the radial direction |
<30% |
|
| Extension in the weft direction |
<30% |
|
| Working Temperature |
Long time 260ºC, Short time 280ºC |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
PTFE impregnation, waterproof or film coating treatment |
Product Description:
PTFE needled felt is a filter material with extremely stable chemical properties, and its characteristics are as follows:
The continuous working temperature is above 260 degrees, and the instantaneous temperature is 280 degrees.
2. It is completely resistant to acids, alkalis and oxidation, and is almost non-flammable.
3. The only fiber that will not age.
4. It can meet the most severe working conditions and has an extremely long service life, usually over three years.
100%PTFE needled felt filter material is mainly applied in the chemical industry, waste incineration, and filtration of highly corrosive liquids, maintaining excellent chemical stability under various complex working conditions.
| Nane |
PTFE Needle Felt |
|
| Material |
PTFE fiber /PTFE base fabric |
|
| Weight |
750±5%g/m² |
|
| Air permeability |
25-45L/dm².min |
|
| Radial tensile force |
>800N/5×20cm |
|
| Weft tensile force |
>700N/5×20cm |
|
| Extend in the radial direction |
<13% |
|
| Extension in the weft direction |
<20% |
|
| Working Temperature |
Long time 260ºC, Short time 280ºC |
| Filteration Air Speed |
≤1.0m/min |
| Treatment |
PTFE impregnation or coating treatment |
Our Advantages
| Product Name |
COLLECTING BAG Chemical Filter Dust Collector |
| Filter Material |
PTFE, PPS Electrostatic Media, High-Temperature Resistant Fiberglass |
| Applicable Factories: |
Flour Mills, Cement Plants, Chemical Plants, Asphalt Plants |
| Advantages: |
We are the manufacturer with competitive pricing and extended service life |
FAQ
FAQ:
1. Are you not sure whether we are a factory or a trader?
Give me three minutes and I'll make a video about our factory for you.
2.Is there any market for our products in your country?
Now all countries attach great importance to environmental protection, so our products are very popular in the market.
3.What are your strengths?
We have our own production line, which means our production costs are low.
In addition, if you are also engaged in online sales, we can provide you with promotional pictures and videos of the product for free.
4.What is the biggest benefit for the buyer to cooperate with you?
We will give the maximum profit to the buyer, which is the most lasting relationship.
We provide online video installation instructions, The tech expert will teach you by video.